Contact fatigue of veneer feldspathic porcelain on dental zirconia

Autor
Rueda, A.O.; Anglada, M.; Jimenez-Pique, E.
Tipus d'activitat
Article en revista
Revista
Dental materials
Data de publicació
2015-03-01
Volum
31
Número
3
Pàgina inicial
217
Pàgina final
224
DOI
https://doi.org/10.1016/j.dental.2014.12.006 Obrir en finestra nova
Repositori
http://hdl.handle.net/2117/76672 Obrir en finestra nova
http://www.sciencedirect.com/science/article/pii/S0109564114006897 Obrir en finestra nova
URL
http://www.sciencedirect.com Obrir en finestra nova
Resum
Objectives. To understand the resistance to cyclic and static contact loading of feldspathic porcelain on dental zirconia (3Y-TZP), in order to understand the partial failure of porcelain (chipping or cracking).; Methods. Hertzian contact techniques were used to evaluate the appearance of damage as a ring crack in terms of applied load and number of cycles in air and simulated saliva.; Results. Static contact loading showed the presence of stress corrosion cracking in the porcelain; the environm...
Citació
Rueda, A.O., Anglada, M., Jimenez-Pique, E. Contact fatigue of veneer feldspathic porcelain on dental zirconia. "Dental materials", 01 Març 2015, núm. 3, p. 217-224.
Paraules clau
Fatigue, Feldspathic dental porcelain, Fracture, Hertzian contact, Zirconia, behavior, brittle solids, ceramics, coatings, crack-propagation, fixed partial dentures, indentation, pumped cone fracture