Microstructural effects on the fatigue crack nucleation in cold work tool steels

Autor
Picas, I.; Cuadrado, N.; Casellas, D.; Goez, A.; Llanes, L.
Tipus d'activitat
Article en revista
Revista
Procedia engineering
Data de publicació
2010-04
Volum
2
Número
1
Pàgina inicial
1777
Pàgina final
1785
DOI
https://doi.org/10.1016/j.proeng.2010.03.191 Obrir en finestra nova
Repositori
http://hdl.handle.net/2117/8471 Obrir en finestra nova
Resum
Crack nucleation mechanisms in two types of cold work tool steels were evaluated under monotonic and cyclic loading conditions. The effect of the microstructural constituents: the primary alloy carbides and the tempered martensite matrix, and their interaction, was identified through fractographic analysis and determination of mechanical properties such as the bending strength, σR, the fatigue limit, Δσfat, and the fracture strength of the primary carbides under static tensile stressing, σRC...
Citació
Picas, I. [et al.]. Microstructural effects on the fatigue crack nucleation in cold work tool steels. "Procedia Engineering", Abril 2010, vol. 2, núm. 1, p. 1777-1785.
Grup de recerca
CIEFMA - Centre d'Integritat Estructural, Micromecànica i Fiabilitat dels Materials
CRnE - Centre de Recerca en Ciència i Enginyeria Multiescala de Barcelona
PROCOMAME - Processos de Conformació de Materials Metàl·lics

Participants